Stainless Steel 403 Furnace Components


Description
Stainless Steel 403 offers heat resistance and a scaling temperature of about 1300°F (704°C). This straight chromium stainless steel offers reasonable corrosion resistance and high mechanical characteristics.


Equivalent
Stainless steel grade 403 equivalent with:
AISI 403, AISI 614, ASTM A176, ASTM A276, ASTM A473, ASTM A314, ASTM A479, ASTM A511, ASTM A580, DIN 1.4000, QQ S763, AMS 5611, AMS 5612, FED QQ-S-763, MIL SPEC MIL-S-862, SAE 51403, SAE J405 (51403), etc



Chemical Composition Stainless 403
Type C Si Mn Cr S P
403 0.15 0.50 1.00 11.5-13.0 0.03 0.04
AISI410 0.08-0.15 1.00 1.00 11.5-13.5 0.03 0.04


Mechanical Properties

Properties
403
Tensile Strength (MPa) 485
Yield Strength (MPa) 310
Elongation (in 50mm) (%)  25
Hardness (HB) 139
Fatigue Strength (MPa) 275
Supplied Condition Annealed


Physical Properties

Properties
403
Density (×1000 kg/m3) 7.80
Elastic Modulus (GPa) 190-210
Thermal Conductivity (W/m-K) 21.5
Poisson's ratio 0.27-0.30
Specific Heat (J/kg-K) 450
Thermal Expansion (┬Ám/m-K) 9.9
Ultimate Resilience (MJ/m3) 77-93


Heat Treatment of Stainless 403
Anneal by heating to 1350° to 1450°F (732° to 78°C), then air cool
To enhance softness, hold at 1450° to 1550°F (788° to 843°C), then furnace cool
Annealing reduces machinability
Harden by quenching from 1750° to 1850°F (954° to 1010°C) in air or oil, then draw between 800° and 1100°F (427° and 593°C)


Machinability of Stainless 403
200-240 Brinell hardness or cold-drawn condition recommended
Use chip curler cutting tools when turning
Grind slight flat on cutting lip face when drilling
Highly concentrated sulfur oil
Turn: 40-80 sfpm
Mill: 35-70
Broach: 8-15
Ream: 20-60
Drill: 30-60


Workability of Stainless 403
May be cold worked
Easily drop or hammer forged
Preheat 2x as long as carbon steel
Preheat to 1400° to 1450°F (760° to 788°C), then rapid heat to 2050° to 2150°F (1121° to 1177°C)
Reheat once temperature drops to 1450° to 1600°F (788° to 871°C)
Bury in dry lime or ash to slow cool



Application
Furnace components
Ladles used in molten nonferrous applications, turbine parts, compressor blades, Stirring rods



Related Steel:

Incoming Search Terms: baja stainless 403, material stainless 403, jual 403, steel aisi403, aisi403 datasheet, equivalen steel, 

Produk Terkait:

Tags:
  • Jual plate Hardox,Bisalloy,Creusabro,XAR wear plate,quard plate, Sumihard,plate raex,JFE Everhard, weldox,Corten,Harga Baja,jual stainless steel,304/L, 316, 310, 3Cr12, Durinox,201,Jual Steel Pipe, distributor baja KS, GG, wear plate, jual steel,harga steel sni terbaru, ASTM,grade,400,500,daftar harga, 2012,jual besi baja,Aluminium plate, material baja preharden,material stavax, jual vcn steel, Harga besi, inp, cnp,unp,WF,H-beam,besi beton,besi cor,Steel AISI,valve, harga,Plate, Boiler,flange,plat Kapal SS400,A36, BKI plate,SPCC, SPHC,Mild steel a36, harga plate sm490 YA, ABS, abrasion,Marine, Offshore plates,DNV,standard,tabel,bolt,nuts,berat